Epoxy Resin Worktop for Laboratory Furniture

• Usage: Hospital, School, Research Institute, Inspection and Quarantine Department
• Color: White, Black, Grey
• Feature: Easy Cleaning, Easy Disinfection, Corrosion Resistance, Abrasion Resistant, Safe
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Material: Epoxy Resin Worktop
• Other Size: 3200X1600mm
• Thickness: 16, 19, 25mm
• Surface Finish: Matte or Polished
• Edge: Marine Edge
• Fabrication: Cutting Sheets
• Transport Package: Plywood Crating
• Specification: 3000x1600mm
• Trademark: MAYEN
• Origin: China
• HS Code: 3920999090
• Production Capacity: 100PCS/Day
• Package Size: 330.00cm * 170.00cm * 36.00cm
• Package Gross Weight: 1800.000kg

Product Description

Company Profile

Zhongshan Mayen Commerce and Trading Co., Ltd. is one of the highly reputed laboratory products suppliers. We have specialized in the development and designing of epoxy resin worktops and sinks, facilitating our customers all over the world with optional solutions under full coverage of safety, sustainability and affordability.
Our products, epoxy resin worktops, epoxy resin sinks, phenolic worktops, water faucets, gas fittings, emergency showers, eye washes, pegboards, extraction arms and other accessories, fume hoods, equipment and lab furniture for laboratory are designed to meet the demands of the industrial, educational, healthcare and pharmaceutical sectors.
Mayen's New Generation epoxy resin worktop adopts the newly developed epoxy resin system, the new production process and the fully automated production process technology. This integrated core epoxy resin worktop is patented, processed by multi-process and high temperature compounding. This matte finish surface epoxy resin worktop is processed by more than 40 fully automated polishing equipment, so it has uniform thickness.
Mayen's New Generation epoxy resin worktop retains the chemical stability, heat resistance and mechanical properties of the traditional epoxy resin worktop. It is of superior corrosion resistance, excellent high temperature resistance, durable reducibility, environmental safety.
Mayen's New Generation epoxy resin worktop strengthens the surface hardness of the product and enhances the mechanical strength and increases the scratch resistance. It improves the production capacity perfectly and increases the molding area of the product. The single piece can be molded into 3200mmx1800mm, which can meet the design and installation of super large laboratory worktop for the projects.


 

Product Description

Standard size:
3000x1600mm
3200x1600mm
-Please contact us for the cutting sheets.

Thickness:
16mm
19mm
25mm

Cutting sheets:
Square
Round
Octagon/Hexagon
Sink module units
- Please contact us for other customized shapes.

Colors:

Black
White
Grey
- Please contact us for other colors.

ADVANTAGES OF MAYEN EPOXY RESIN WORKTOPS

DURABILITY
MAYEN epoxy resin worktops are monolithic and non-porous; they do not delaminate or swell. They are easy to install on site.

APPEARANCE
MAYEN epoxy resin worktops have a smooth and matte surface that is easy to clean and maintain.

CHEMICAL RESISTANCE
MAYEN epoxy resin worktops are highly resistant to the corrosive effects of most chemicals and organic solvents and compounds.

HEAT RESISTANCE
MAYEN epoxy resin worktops will not blister or crack when exposed to extreme temperatures in the laboratory.

SAFETY
MAYEN epoxy resin worktops are enhanced by a natural, asbestos-free additive, providing fire resistance and insulation properties in a user-safe environment.

INDOOR AIR QUALITY
MAYEN epoxy resin worktops are low-emission certified.




 

CHEMICAL RESISTANT PROPERTIES TESTING

Method A
Used for Volatile Chemicals (organic solvent):
A cotton ball, saturated with the test chemical (reagent), is placed in a 1-ounce test tube with a reservoir of liquid above the ball. The container is inverted on the test material at a standard temperature of 23ºC plus or minus 2ºC (73°plus or minus 4ºF).

Method B
Used for Non-Volatile Chemicals:
5 drops (1/4cc) of the test chemical are placed on the test material surface. The chemical is covered with a watch glass (d=5cm) at a standard temperature of 23°plus or minus 2ºC (73°plus or minus 4ºF).

For both the above methods (A and B), leave the reagents on the panel for a period of: 1 hour for exposed vertical surfaces and semi-exposed surfaces, 24 hours for exposed horizontal surfaces such as countertops. After exposure, exposed areas are washed with water, then a detergent solution, finally with naphtha, then rinsed with distilled water and dried with a cloth.
 

Chemicals	Concentration	Method	Test Result
Inorganic Acids - Corrosive
Chromic Acid (CrO3)	40%	B	1
Hydrochloric Acid (HCL)	10%	B	1
Hydrochloric Acid (HCL)	37%	B	1
Nitric Acid (HNO3)	40%	B	1
Nitric Acid (HNO3)	70%	B	1
Sulfuric Acid (H2SO4)	40%	B	1
Sulfuric Acid (H2SO4)	96%	B	3
Hydrofluoric Acid (HF)	48%	B	3

 

Organic Acids - Corrosive
Acetic Acid (CH3CO2H)	5%	B	1
Acetic Acid (CH3CO2H) - Glacial	99%	B	1
Citric Acid (C6H8O7)	1%	B	1
Oleic Acid (C18H34O2)	Original	B	1
Phenol Solution (C6H5OH)	5%	B	1

 

Alkaline Solutions - Corrosive
Ammonium Hydroxide (NH4OH)	10%	B	1
Potassium Hydroxide(KOH)	15%	B	1
Sodium Carbonate Sol (Na2CO3)	20%	B	1
Sodium Hydroxide Sol (NaOH)	60%	B	1
Sodium Hypochlorite Sol (NaOCI)	4%	B	1

 

Organic Solvents
Acetone (CH3COCH3)	Original	A	2
Benzene (C6H6)	Original	A	2
Carbon Tetrachloride (CCI4)	Original	A	1
Diethyl Ether (CH3CH2OCH2CH3)	Original	A	1
Dimethyl Formamide (HCON[CH3]2)	Original	A	1
Ethyl Acetate (CH3CO2C2H5)	Original	A	2
Ethyl Alcohol (CH3CH2OH)	Original	A	1
Etheylene Dichloride (CICH2CHCI)	Original	A	1
Heptane (CH3[CH2]5CH3)	Original	A	1
Isooctane (C8H18)	Original	A	1
Kerosene	Original	A	1
Methyl Alcohol (CH3OH)	Original	A	1

 

Organic Compounds
Aniline (C6H5NH3)	Original	B	2
Mineral Oil	Original	B	1
Olive Oil	Original	B	1
Soap Solution	1%	B	1
Transformer Oil	Original	B	1
Turpentine	Original	B	2

Test Evaluation
The effect on the surface of the specimen is inspected visually and express in accordance with the following rating scale:

1	No effect	: No detectable change in the material surface.
2	Excellent	: Slight detectable change in colour or gloss, but no change to the function or life of the work surface material.
3	Good	: Clearly discernible change in colour or gloss, but no significant impairment of surface life or function.
4	Fair	: Objectionable change in appearance due to surface discoloration or etch, possibly resulting in deterioration of function over an extended period.
5	Failure	: Pitting, cratering or erosion of work surface material; obvious and significant deterioration.

 

PHYSICAL PROPERTIES TESTING

 

Physical Properties	Test Standard	Tested Data
1a. Specific Gravity, average	ASTM D792 : 2000 ASTM D792 : 2000	2.24
1b. Density (g/cm³), average		2.24
2.  Rockwell Hardness (M Scale), average	ASTM D785 : 2003	125
3.  Heat Deflection Temperature (ºC), average	ASTM D648 : 2007	243 ºC
4a. % Water Absorbed, average	ASTM D570 : 1998(2005) ASTM D570 : 1998(2005) ASTM D570 : 1998(2005)	0.010
4b. % Increase in Weight, average		0.010
4c. % Soluble Matter Loss, average		None
5.  Flammability (Horizontal)	ASTM D635 : 2003	Not flammable
6.  Compressive Strength (Mpa), average	ASTM D695 : 2002                   ASTM D638 : 2003	211.9
7a. Maximum Tensile Strength (Mpa), average		58
7b. Tensile Modulus (Mpa), average	ASTM D638 : 2003	12618
8a. Flexural Strength (Mpa), average	ASTM D790 : 2003 ASTM D790 : 2003	98.7
8b. Flexural Modulus (Mpa), average		10929

MAINTENANCE AND REPAIR
MAYEN epoxy resin worktops will not stain and are resistant to most abrasive chemicals. Periodic cleaning with a 70% ethyl alcohol solution is recommended (other waxes or coatings should not be applied). MAYEN epoxy resin worktops can suffer damage however through abuse or neglect. Scratches and marks can usually be repared on site using the following materials and procedure:

Material required:
• Oil (mineral or light machine oil)
• Silicone Carbide Sandpaper (grits 80, 120 and 220)
• 3M Scotch Brite (or equivalent)
• Clean cloths
Depending on field conditions, either hand-tools or power-tools may be used to repair scratches.

Procedure:

1. Apply oil to the area to be repaired, then begin sanding with 80 grit sandpaper in the same direction as the scratch using a moderate to light touch until scratch disappears. The lighter the pressure, the less material is removed, and the better the repair will look.
2. The final sanding should be done using 220 grit paper and oil. Again, work in the same direction as the scratch using a light touch. Use plenty of oil to remove sanding marks from the work surface. Buff the sanded area with oil and 3M Scotch Brite until you are satisfied with the result. Buff further with clear rags and the repair is complete.

 

Detailed Photos

 

 

Packaging & Shipping

 

plywood crating










 

FAQ

 

Q1. Why choose us?
A1. We are the leading laboratory products supplier, OEM & ODM service are offered.
 
Q2. What's MAYEN main products?
A2. We supply epoxy resin worktops, epoxy resin sinks, phenolic worktops, water faucets, gas fittings, emergency showers, eye washes, pegboards, extraction arms and other accessories, fume hoods, equipment and lab furniture for laboratory.
 
Q3. How about the sample?
A3. We could send you the samples but the freight is collect.
 
Q4. How about the payment term?
A4. T/T & L/C  (50% deposit, the balance before shipment).
 
Q5. How about the delivery time?
A5. Within 7-15 workdays after receiving deposit.
 
Q6. How about the validity of quotation?
A6. Usually 60 days as the shipping freight and exchange rate can be fluctuant.
 
Q7. What is the shipping port?
A7. FOB to Guangzhou or Shenzhen Port,China(also can ship according to customers' request).
 
Q8. How about the package?
A8. Wooden crating or carton.
 
Q9. How to inspect the goods?
A9. Products will checked by our QC staff first, then our proejct manager. Client can come and check by themselves or by the third party.